The preparation method of perlite lightweight ceramic materials

用于化工填料、催化剂载体、过滤设备、保温设备、隔音设备、散热设备的轻质陶瓷材料。轻质陶瓷材料的配方包括镁质粘土、漂珠、珍珠岩粉、成孔剂和粘结剂，经配料、球磨、榨干、成型、烘干、烧结而成。

Used in chemical industry packing, catalyst carrier, filtration equipment, thermal insulation, sound insulation, heat dissipation of lightweight ceramic materials.Lightweight ceramic materials formula including magnesian clay, drift beads, perlite, pore forming agent and bonding agent, the ingredients, ball mill, drains, molding, drying, sintering and into.

它有重量轻、耐热、耐寒、高强度、抗腐蚀性强、不变形、保温隔热性能好、隔音性能好、成本低、制作方便等优点，可替代普通陶瓷、木、金属、塑料制品。

It has light weight, heat resistant, cold resistant, high strength, strong corrosion resistance, deformation, heat preservation and heat insulation performance is good, good sound insulation performance, low cost, convenient production, alternative to the ordinary ceramic, wood, metal, plastic products.
轻质陶瓷材料，其特征在于由镁质粘土、漂珠、珍珠岩粉、成孔剂、粘结剂组合烧结而成，它们的重量份数配方是镁质粘土 20～70％，漂珠1～50％，珍珠岩粉1～30％，成孔剂1～30％，粘结剂 1～50％，主要化学组成成分为SiO2、A12O3、MgO，其中SiO2的量为 50～85％(重量)，A12O3的量为5～25％(重量)，MgO的量为5～25％(重量)，本发明所含有的其它组分可能进一步包括Fe、Ca、K、Na、Ti 等金属的氧化物。

Lightweight ceramic materials, its characteristics is by magnesian clay, drift beads, perlite, pore forming agent, binder, sintering and their weight number formula is 20 ~ 70%, magnesian clay drift beads 1 ~ 50%, perlite 1 ~ 30%, and 1 ~ 30% pore forming agent, binder 1 ~ 50%, the main chemical composition is SiO2, A12O3, MgO style, including the amount of SiO2 is 50 ~ 85% (weight), the amount of A12O3 for 5 ~ 25% (weight), the amount of MgO style for 5 ~ 25% (weight), the invention of other components may further include Fe, Ca, K, Na, Ti and other metal oxides.